Ceramic Honeycomb Catalyst Substrate Catalytic Converter for

• Customization: Available
• Application: Catalyst carriers
• Cell Shape: Square
• Model NO.: Honeycomb ceramics
• Material: Cordierite
• Temperature Resistance: 800℃
• Transport Package: Cardboard Box/Wooden Pallet
• Specification: 100-400Ccpsl
• Trademark: JJXY
• Origin: China
• HS Code: 690911000
• Production Capacity: 100000

Product Description

Product Description

 

VOC catalytic combustion process
Organic waste gas reacts directly with oxygen in the air, requiring a temperature above 700 ºC and sufficient residence time. However, under the action of catalysts, the activation energy of organic compounds reacting with oxygen can be greatly reduced, while the reactants are enriched on the surface of the catalyst, providing a translation rate. With the help of catalysts, organic waste gas can undergo flameless combustion at lower ignition temperatures (100 ºC -400 ºC), and be oxidized and decomposed into carbon dioxide and water vapor, while releasing a large amount of heat energy.

Detailed Photos

 

Product Parameters

 

project
Thermal shock resistance	Keep at800 ºC for 30 minutes, quickly remove and cool at room temperature for 30 minutes. Repeat this process continuously for 3 times		muffle furnace
compressive strength	A-axis	>=10Mpa	Compression strength machine
	B-axis	>=1.4Mpa
Thermal expansion coefficient (room temperature -800 ºC)	≤ 1.0 * 10-6/ºC (A-axis).		Thermal expansion coefficient meter
Water absorption rate	20%-26%		Electronic scale
Content of main crystal phase in cordierite	>=90%		XRD
chemical composition	AL203	(49.7±1.5)%,
	Mg0	(13.5±1.5)%;
	Si02	SiO2=(35.4±1.5)%,
Maximum softening temperature	>=1360ºC
verticality	Height ≤ 100 mm, verticality ≤ 1 mm; Height>100
Parallelism	Diameter ≤ 100mm, tolerance ≤ 1mm; Diameter>100mm, tolerance ≤ 1% of product outer diameter dimension.