Customization: | Available |
---|---|
Cell Shape: | Square |
Material: | Cordierite |
Still deciding? Get samples of US$ 1/Piece
Request Sample
|
Suppliers with verified business licenses
Audited by an independent third-party inspection agency
VOC catalytic combustion process
project | |||||
Thermal shock resistance | Keep at800 ºC for 30 minutes, quickly remove and cool at room temperature for 30 minutes. Repeat this process continuously for 3 times | muffle furnace | |||
compressive strength | A-axis | >=10Mpa | Compression strength machine | ||
B-axis | >=1.4Mpa | ||||
Thermal expansion coefficient (room temperature -800 ºC) | ≤ 1.0 * 10-6/ºC (A-axis). | Thermal expansion coefficient meter | |||
Water absorption rate | 20%-26% | Electronic scale | |||
Content of main crystal phase in cordierite | >=90% | XRD | |||
chemical composition | AL203 | (49.7±1.5)%, | |||
Mg0 | (13.5±1.5)%; | ||||
Si02 | SiO2=(35.4±1.5)%, | ||||
Maximum softening temperature | >=1360ºC | ||||
verticality | Height ≤ 100 mm, verticality ≤ 1 mm; Height>100 | ||||
Parallelism | Diameter ≤ 100mm, tolerance ≤ 1mm; Diameter>100mm, tolerance ≤ 1% of product outer diameter dimension. | ||||